4. 201 (1.4372) STAINLESS STEEL
201 (1.4372) Chemical composition (%)
| ITEM | Ni | Cr | Cu | Mn | Si | C | N | P | S |
|---|---|---|---|---|---|---|---|---|---|
| Min | 0.80 | 14.00 | 1.30 | 8.00 | === | === | === | === | === |
| Max | 1.30 | 17.00 | 2.00 | 10.00 | 1.00 | 0.15 | 0.25 | 0.06 | 0.03 |
201 (1.4372) Mechanical properties
| Min | Max | ||
|---|---|---|---|
| Yield Strength (N/mm2) | 0.20% Y.S. | 310 | N/mm2 |
| 1% Y.S. | === | ||
| Tensile Strength (N/mm2) | 665 | N/mm2 | |
| Elongation % | 30 | === | |
| Hardness Test | HRB | === | 105 |
| HV | === | 300 | |
202 (1.4373) STAINLESS STEEL
202 (1.4373) Chemical composition (%)
| ITEM | Ni | Cr | Cu | Mn | Si | C | N | P | S |
|---|---|---|---|---|---|---|---|---|---|
| Min | 3.50 | 17.00 | 1.30 | 5.50 | === | === | 0.05 | === | === |
| Max | 5.50 | 18.00 | 1.80 | 7.50 | 1.00 | 0.15 | 0.25 | 0.045 | 0.015 |
202 (1.4373) Mechanical properties
| Min | Max | ||
|---|---|---|---|
| Yield Strength (N/mm2) | 0.20% Y.S. | 260 | N/mm2 |
| 1% Y.S. | === | ||
| Tensile Strength (N/mm2) | 640 | N/mm2 | |
| Elongation % | 40 | === | |
| Hardness Test | HRB | === | 100 |
| HV | === | 260 | |